Plastic, Plastic Raw Material, Clear Nylon manufacturer / supplier in China, offering Plastic Raw Material Clear Polyamide Tr Material Plastic, PA612 Spinning, PA610 Granules Spinning and so on.

Gold Member Since 2017
Audited Supplier
Supplier Homepage Products Transparent Nylon Plastic Raw Material Clear Polyamide Tr Material Plastic

Plastic Raw Material Clear Polyamide Tr Material Plastic

Get Latest Price
Min. Order / Reference FOB Price
500 kg US $14/ kg
Port: Qingdao, China
Production Capacity: 6000t/Year
Payment Terms: L/C, T/T
Material: PA12
Usage: Specialty Plastics
Plastic Properties After Heated: Thermoplastic Plastics
Plastic Forming Method: Injection
Color: Transparent
Transport Package: White Kraft

You Might Also Like

Loading...

Basic Info

Model NO.
CXT8113
Origin
Shandong
HS Code
3908101910
LEADER OF TRANSPARENT NYLON                            
 
 
 
 
 
 
 
 
 
CXT8113 natural is a high purity, high transparency, amorphous, thermoplastic polyamide, based on cycloaliphatic monomers. Compared with semi-crystalline nylon, CXT8113 avoid crystallizing by selecting specific monomers and becomes an other amorphous polymer which has high transparency. Meanwhile, CXT8113 combine the properties of semi-crystalline nylon and amorphous nylon which makes it be the first choice in the present market.
 

 
It is available in the form of small, free flowing pellets in 20 kg foil-lined bags.
 

 
Commercial, Active, Globally
 
 
 
Composition                PAMACM12
 
  1. Permanent transparency and high light transmission
  1. High dimensional stability and easy processing
  1. Excellent abrasion and scratch resistance
  1. Superior impact resistance to high / low temperature 
  1. Good chemical and solvent resistance
  1. High level of UV resistance and weathering stability
  1. High stress crack resistance
  1. High flexural fatigue strength and high memorability
  1. Low density and light quality
  1. Easily colorable and food contact approval
Features                     
 
 
 
 
 
 
 
 
 
 
 
 
Disclaimer
-Data shown are typical values obtained by proper testing methods and shoud not be used for specification purpose.
-In addition, the information supplied is not guarantee value, so please consider fully operational environment and product design.
    -Put into use after safety confirmation of this product, From the negative consequences own responsibility!

 
Optics Packaging
 
Frames, Lens, Optical components etc.
 
  
Cosmetics packaging, Medical packaging, etc.
Food Contact Industry
 
Feeder, Coffee machine, Cup, etc.
 
 
 
 
Auto parts(oil cup, etc), Mechanical engineering.
Ectronic Products Consumer Goods
 
Headphone, Ear-Hook, etc.
  
Sports & Leisure, Tools & Accessories, etc.
 

 
Notes                 CXT8113 has been fully dired before they leave the factory and the moisture content ≤1‰. It can be bring on stream directly in case of undamaged packaging.
Don't expose the material to air for long time or damage the packaging to protect the materials from absorbing the moisture in the air. High moisture will cause overflowing of the molten materials during the process and the generated bubbles will form the ripple on the surface of products.
It should be stored in dry warehouse at 25ºCwith the perfect seal and packaging. This material will be oxidized and yellowed as the storage temperature is long-term higher than 25ºC
Drying MachineryDrying Temperature (ºC)Time(h)
Vacuum Dryer80--1006--8
 
Process of Drying                                     
                                                  
 
Equipment Requirement       CXT8113 is an amorphous nylon resin which can be processed on conventional extrusion, coextrusion, injection molding or blow molding equipment that is designed to process nylon or polyolefin resins.
 
Screw                         We recommend to use the anti-wear protection, with a one-way valve nozzle, general purpose (3 heating zone) screws. 
Length: 18D - 22DCompression Ratio:  2 - 2.5
Disclaimer
-Data shown are typical values obtained by proper testing methods and shoud not be used for specification purpose.
-In addition, the information supplied is not guarantee value, so please consider fully operational environment and product design.
    -Put into use after safety confirmation of this product, From the negative consequences own responsibility!
Injection Volume                 Injection volume must be longer than shoot back in the absence of return flow metering. Maximum mold filling capacity: approximately maximum injection volume × 0.5-0.9
 
Heating Section            There must be at least three independent heating zones with independent temperature regulation in order to make the temperature be able to reach 350°C, meanwhile, the feed nozzle temperature must be adjustable (cooling device).
 
Nozzle                        While the open nozzles are simple, flowable and durable, it will intake air and generate oxidation reaction when the screw goes through the metering section, so, the needle valve nozzle is suggested.
 
Calculation: 7.5 kN1) x cavity projected area (cm²)
Clamping Force                       
 
 
Mould                     Mould design principles are same as transparent thermoplastic plastic.Typically the cavity steel must reach 56HRC and anti-abrasion measures  is recommended in the high-speed flow mold portion.
 
Gate and Runner           In order to accomplish the desired dosing and avoid shrinkage of finished product, it is recommended to set the gate in the center of the thickest part, pin point gate and tunnel gate are more economical, but the mold design requires a higher technical level.
Gate size: 0.8×maximum wall thickness
Runner size:1.4×maximum wall thickness
 
 
Process                         The high injection speed and extension of pressure time is needed in order to get a better surface and a stronger joint line . Injection speed should be properly adjusted to avoid the excessively high injection speed during the end of molding cycle. Cooling time should be sufficient under the low speed and low pressure .
 
 
 
Disclaimer
-Data shown are typical values obtained by proper testing methods and shoud not be used for specification purpose.
-In addition, the information supplied is not guarantee value, so please consider fully operational environment and product design.
    -Put into use after safety confirmation of this product, From the negative consequences own responsibility!
Exhaust                       It is imperative to give full consideration to the adequate exhaust and more adequate exhaust is suggested at the joint line. The polishing size at least 0.2mm.
 

 
Feed section100ºC
Heating section 1235ºC
Heating section2240ºC
Heating section 3255ºC
Nozzle240ºC
Mold80ºC
Melt245ºC
 
 
 
Temperature Settings
 
 
 
 
 
Injection speedMiddle ---High
Hold-on pressure30---60(MPa)
Backpressure0.5---1(MPa)
Screw speed50-100 min-1
 
                   
Pressure Speed Settings
 
 
 
 

 
ItemsUnitTest MethodValues
Charpy notched impactKJ/m²GB/T 1043-9317
Charpy non-notched impactKJ/m²GB/T 1043-9325JNB
Tensile strengthMPaGB/T 1040-9265
Elongation at break%GB/T 1040-92160
Flexural strengthMPaGB 9341-200070
Flexural modulusMPaGB 9341-20001780
Densityg/cm³GB 1033-861.01
Heat distortion temperature(0.45 MPa)ºCGB1634-79135
Light transmittance%--92
Shore D hardness--GB 2411-8083
 
 
 
 
 
Disclaimer
-Data shown are typical values obtained by proper testing methods and shoud not be used for specification purpose.
-In addition, the information supplied is not guarantee value, so please consider fully operational environment and product design.
    -Put into use after safety confirmation of this product, From the negative consequences own responsibility!

 
 
EU certification     CXT8113 transparent nylon resin is up to the standard of RoHs, REACH and possesses the non-polycyclic aromatic hydrocarbons(PAHS) test report. It also meets requirements of SVHC and can be applied in the area of food contact, water contact product.
 
Safety & Handling            CXT8113 has no irritation for skin. We should adopt enough ventilation to remove the smoke that may hurt peoples' eyes, nose, throat, and upper respiratory tract in the work area. Mind your hands and other exposed parts of the body under high-temperature processing. If molten resin exposed to the skin, apply cold water or ice to lower the contact parts. Don't try to stripped solidified resin from the skin and the burned area should be treated. Cleaning timely the scattered resin particles to prevent the pedestrian from falling because of its slippage.                          
 
It has no special requirements for the  processing of waste, we can process by sanitary landfill or put into the incinerator. Disposal of waste should comply with regional, provincial and national regulations.
 
 
 
 
 
 
Disclaimer-
-Data shown are typical values obtained by proper testing methods and shoud not be used for specification purpose.
     -In addition, the information supplied is not guarantee value, so please consider fully operational environment and product design.
         -Put into use after safety confirmation of this product, From the negative consequences own responsibility!
 

Send your message to this supplier

*From:
*To:
avatar Miss Alisa
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

You Might Also Like

Loading...

Contact Supplier

Miss Alisa
Sales Manager